LG PVCPB1752
型号：PB1752 用途：Tarpaulin, top layer for flooring, farbric coating 包装：20Kg 产地：德国
LG PVC PB1752
PB1752, homopolymer made from micro-suspension poiymerization,is a low-viscosity PVC resin with a peseudo ptastic flow property in processing range.
PB1752 can be used for skin layer for flooring, tarpaulin made by Knife coating/rotary screen coating especially,products made from PB1752 are excellent in transparency, matting and physical properties.
Application
Tarpaulin, top layer for flooring, farbric coating
Properties
| Item | Test Method | Unit | Test Condition | Value |
| Degree of Polymenzation | JIS K 6721-77 | - | 30°C | 1700±1OO |
| K-Value | DIN 53726 | - | - | 79 |
| Apparent Bulk Oensity | ASTM D1895-90 | g/cm2 | - | 0.36±0.06 |
| Volatiles | ASTM D3030-90 | % | 110°C x lhr | Max 0.2 |
| Brookfied Viscosity(DOP 60phr) | ASTM D1824-90 | cps | 6 RPM | |
| Sever Visco sity(DOP 60phr) | ASTM D3030-90 | g/sec | 4 BAR | Min 0.2 |
*Note:
1)The values of properties in the above table have been obtained by the test pieces(natural color) manufactured under certain of injection.
2)The listed values should be used for referential purposed only
Test Condition
1) Brookffefd Viscosity
Fomulation Resin 100, DOP refer to chart
Condition
Rotational Viscometer
Mode LVT Type, Rotor RPM 6, 12
2) Severs Vscosity
Condition
Severs Extrusion Rheometer
Orifice diameter 3.043mm,Iength 50mm
Pressure 4, 8 Bars
Contact the technical team of PVC & Plasticizer any questions or requirements relevant to PB1752 products.